Non heat sealable, both sides treated super white opaque biaxially oriented polypropylene label film, suitable for:
Rotogravure and flexographic printing.
Cut & stack and reel fed labeling applications.
Outstanding opacity and bright white background.
CHARACTERISTICS
Outstanding opacity and bright white background.
Excellent stiffness.
High gloss.
Excellent printability and receptivity to adhesives.
Improved resistance to label tearing.
Good mould resistance.
Low density and high yield.
APPLICATIONS
Labelling of mineral water, juice, carbonated beverages and oil bottles.
Properties unit Test method Tolerance Typical value

Thickness

micron

--

±4%

38 42 47 70

Yield

m²/ kgm -- ±4% 34.17 30.92 27.63 18.55
Unit weight gm/m² -- ±4% 29.26 32.34 36.19 53.9

Tensile strength

MD
TD
N/mm² ASTM D 882
Min.
Min.
60 60 60 60
130 130 130 130

Breaking elongation

MD
TD
% ASTM D 882

± 20

± 10

135 135 135 135
30 30 30 30

Modulus of elasticity

MD
TD
N/mm² ASTM D 882
Min.
Min.
1000 1000 1000 1000
1700 1700 1700 1700

Heat
shrinkage

MD
TD
% In air, in oven
For 5 min.
At 130 ºC
Max.
Max.
4 4 4 4
2 2 2 2
Optical
density
% Tobias Denstiometer Min. 0.65 0.68 0.7 0.75
Gloss G.U. ASTM D 2457 Min. 100 100 100 100
Coefficient of friction -- ASTM D 1894

± 0.05

0.4 0.4 0.4 0.4
Water vapour permeability g/m².24 hrs
at 38 ºC
90% RH
ASTM E
96-66
BS 3177
Max. 5.2 4.8 4.5 3.5
Oxygen permeability cc/m². 24hrs Bar, at 23ºC,
0% RH
ASTM D
1434
Bs 2782 –
514 A
Max. 1550 1450 1300 1100
Wetting tension dyne / cm ASTM D 2578

± 2

40 40 40 40
Denisty Kgm/m³ ASTM D 1505

± 0.05

0.77 0.77 0.77 0.77

 

TOP